Authentic Dental GC 1 Gold Label Lutting & Lining cement | Mini | Long Expiry

Description

Features
·
Intrinsic chemical adhesion to both tooth structure and metal
·
Glass Ionomer formulation
·
Fluoride release
·
High mechanical strength
·
Excellent wetting properties
·
Film thickness of just 15 microns
·
Radiopaque
·
Sharp set characteristics
·
Low solubility
·
Long term clinical data
·
No surface preparation or bonding agent required
·
Easy post-operative checks
Description
A Strontium-based Glass Ionomer:
·
All GC Gold Label Glass Ionomer contains strontium glass.&The strontium glass provides good radiopacity and snapset& characteristics, unanimously preferred by clinicians around the world. Interestingly, strontium will mimic calcium& in the formation of strontium hydroxyapatite and strontium& fluoroapatite to affect internal& remineralization within the& tooth structure.
·
Surface Strengthening Effect:
·
Research has shown that a strontium-based glass ionomer placed in calcium-containing environment (saliva) will result in calcium ion diffusing into the glass ionomer&surface achieving a surface strengthening effect. All GC& Gold Label Glass Ionomer strengthens over time in saliva.
·
A Consistent Predictable Seal:
<
·
All GC Gold Label Glass Ionomer will display a glossy& surface after mixing. This indicates sufficient free polyacrylic acid is available to begin the ion exchange process. The& subsequent movement of ions between dentin, enamel and& GC Glass Ionomer creates an ion exchange zone which chemically fuses them together. The resulting seal is& consistent, predictable and long lasting.
INDICATIONS :
·
Cementation of metal or porcelain fused to metal crowns, bridges, inlays
·
Cementation of stainless steel crowns or orthodontic appliances retained with stainless steel crowns
·
Cementation of orthodontic bands
·
Base or liner
ADVANTAGES:
·
Allows minimal cavity preparation
·
Less stress on margins and marginal seal
·
Protects against secondary caries
·
Promotes internal remineralization and surface strengthening
·
Easy post-operative diagnosis
·
Easier mixing and sharper setting makes it so easy to use
·
Final finish may be completed under water 15 minutes from start of mix
·
Matches to natural tooth structure
·
Good colour match to tooth structure
·
More durable, longer lasting restorations
·
Assurance of successful restorations
Key Specifications
Composition / Information on Ingredients
(% chemical components by WT)
·
Distilled water
(CAS 7732-18-5) 50-55%
·
Polyacrylic acid
(CAS 9003-01-4) 30-40
Store at temperature of
4-25°C (39.2-77.0°F)
Powder/liquid ratio (g/g)
1.4/1.0
1.8/1.0
2.2/1.0
Mixing time (min. sec.)
20"
20"
20"
Working time (min. sec.)
2’30"
2’00"
1’15"
Net setting time (min. sec.)
2’50"
2’30"
2’20"
PRECAUTIONS
·
In case of contact with oral tissue or skin, remove immediately with a sponge or cotton soaked in alcohol. Flush with water.
·
In case of contact with eyes, flush immediately with water and seek medical attention.
·
DO NOT mix powder or liquid with any other glass ionomer components.
Packaging
Gc Gold Label 1 Glass Ionomer Mini Pack:
·
1 x 15g Powder
·
1 x 10g Liquid
Direction to Use
STEP1-
Mix to the correct powder:liquid ratio (20 seconds for Gold Label 1)
STEP2-
Apply the mixed cement to both restoration and prepared tooth
STEP3-
Seat the restoration within 30 seconds of completing the mix
STEP4-
Remove the excess cement during the gel stage
Total setting time is 4’30” after start of mix
STEP5-
After final set, moisture proof the margin by applying a final coat of GC Fuji Varnish or GC Fuji Coat LC